Hydrothermal carbonization (HTC) of pure cellulose (CE) and birchwood (BW) samples was carried out at temperatures between 160 and 280 °C, 0.5 h residence time and biomass-to-water ratio 1:5, to investigate the reactivity of cellulose in lignocellulosic biomass. Thermogravimetric analysis (TGA) and Fourier transform infrared spectroscopy (FTIR) showed that the CE samples remained unaltered at temperatures up to 220 °C, but were significantly decomposed at 230 °C producing a thermal recalcitrant aromatic and high energy-dense material. FTIR showed that dehydration and aromatization reactions occurred at temperature equal or higher than 230 °C for the CE samples while a similar increase in aromatization for the BW hydrochars was evident only at temperatures equal or higher than 260 °C. Acid hydrolysis, TGA and FTIR suggested that a higher thermal resistance of naturally occurring cellulose in BW (when compared to CE sample) could be related to a ‘protecting shield’ offered by interlinked lignin in the plant matrix.

Reactivity of cellulose during hydrothermal carbonization of lignocellulosic biomass

Maurizio Volpe;Antonio Messineo;
2020

Abstract

Hydrothermal carbonization (HTC) of pure cellulose (CE) and birchwood (BW) samples was carried out at temperatures between 160 and 280 °C, 0.5 h residence time and biomass-to-water ratio 1:5, to investigate the reactivity of cellulose in lignocellulosic biomass. Thermogravimetric analysis (TGA) and Fourier transform infrared spectroscopy (FTIR) showed that the CE samples remained unaltered at temperatures up to 220 °C, but were significantly decomposed at 230 °C producing a thermal recalcitrant aromatic and high energy-dense material. FTIR showed that dehydration and aromatization reactions occurred at temperature equal or higher than 230 °C for the CE samples while a similar increase in aromatization for the BW hydrochars was evident only at temperatures equal or higher than 260 °C. Acid hydrolysis, TGA and FTIR suggested that a higher thermal resistance of naturally occurring cellulose in BW (when compared to CE sample) could be related to a ‘protecting shield’ offered by interlinked lignin in the plant matrix.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11387/138902
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 49
  • ???jsp.display-item.citation.isi??? ND
social impact